Flame-Retardant Polyester Fiber Compositions

ABSTRACT

Flame-retardant polyester fibers containing 5 to 20 percent by weight of phosphate triester containing at least one mole of a hydroxymethyl bicyclic phosphate and 0-2 moles of a phenyl or naphthyl aryl compound as the sole flameretardant additive or a two-component additive comprising the aforesaid triester in admixture with 20 to 80 percent of certain polychlorinated or polybrominated diaryl compounds.

Lam -h5g1? 5 XE 3 9 883 a 478 o t' :F- E I m United Stat [111 3,883,478 Gresham May 13, 1975 FLAME-RETARDANT POLYESTER FIBER [56] References Cited COMPOSITIONS UNITED STATES PATENTS [75] Inventor: John T. Gresham, Somerset, NJ. 3,459835 8/1969 Dever et al. 260/45.8 R

. 7 Assigneez FMC Corporation, New York. NY 3.6241124 11/1971 Caldwell et al. ..6()/45.7 R [22] Filed: Dec. 7, 1973 Primary Examiner-Melvyn l. Marquis 21 A l. N 422,841 PP O 57 ABSTRACT l Flame-retardant polyester fibers containing 5 to 20 [52] U.S. Cl. 260/458 R, 8/21 B, 8/21 C, percent by weight of phosphate triester containing at 1 2 5; g 2 i Z2g g' g 4 6: least one mole of a hydroxymethyl bicyclic phosphate /4 8( and 02 moles of a phenyl or naphthyl aryl compound Int cl 6 as the sole flameretardant additive or a twocomponent additive comprising the aforesaid triester [58] g ig gg'fi g i' g j in admixture with 20 to 80 percent of certain poly- 5 chlorinated or polybrominated diaryl compounds.

FP; 8/21 B, 21 C; 57/140 BY 14 Claims, No Drawings FLAME-RETARDANT POLYESTER FIBER COMPOSITIONS This invention relates to flame-retardant polyester fiber compositions. More particularly, this invention relates to flame-retardant polyester fibers which contain, as the flame-retardant additive, a complex phosphate triester.

Polyester compositions containing organic phosphorus and organic halogen compounds are known and are disclosed, for example, in U.S. Pat. Nos. 3,356,631 issued Dec. 5, 1971, to Jackson et al.; 3,645,962 issued Feb. 29, 1972, to Schwarz; 3,681,281 issued Aug. 1, 1972, to Juelke et al.; 3,688,001 issued Aug. 29, 1972, to Exner et al.; 3,708,328 issued Jan. 2, 1973, to Kelkheim et al., West German Pat. No. 2,001,125 (1970) to Caldwell et al. (Eastman Kodak Company), and U.S. Pat. No. 3,658,634 issued Apr. 25, 1972, to Yanagi et al. Bicyclic derivatives of phosphorus are known and are described, for example, in U.S. Pat. Nos. 3,293,327, issued Dec. 20, 1966 to l-lechenbleikner et al. and 3,310,609, issued Mar. 21, 1967 to Baranauckas et al.

The various prior art flame-retardant polyester fiber compositions have a number of disadvantages in that they are either uneconomical for commercial use, or the additive is not compatible with molten polyester or is reactive with it, or the desired degree of flame retardancy is not obtained at suitable levels of concentration. It has always been desirable to provide efficient, but compatible flame-retardant additives which can be successfully incorporated into the molten polyester prior to the formation of fibers. Moreoever, a particular problem in the art has been successfully providing flame-retardant polyester fibers which, when blended with other fibers, retain their flame retardant characteristics and impart to the finished fiber blend a high degree of flame retardancy.

According to the present invention, there are provided flame-retardant polyester fiber compositions comprising from about 95 to 80 parts by weight of a fiber-forming linear polyester and to 20, preferably to 15, parts by weight of a phosphate triester flameretardant additive having the formula car-0 y where R is an aryl radical selected from the group consisting of phenyl and naphthyl radicals and phenyl and naphthyl radicals containing 1 to 3 chlorine or bromine atoms and substituted derivatives of these radicals the substituents being methyl, methoxy, phenyl, phenoxy and phenyl and phenoxy containing 1 to 5 chlorine or bromine atoms, and y is an integer from 1 to 3, preferably 1 or 2, and x is 3-y. The latter described preferred embodiments, that is, those complex mixed phosphate triesters which contain one or two of the aforesaid aryl radicals are believed to be novel compounds and, as such, constitute a further embodiment of the present invention.

The complex phosphate triester flame-retardant additives of the present invention are readily prepared from the intermediate hydroxymethyl bicyclic phosphate, which is formed from pentaerythritol and triethyl phosphate in a two-step reaction as described in U.S. Pat. No. 3,293,327. The intermediate is then reacted with the appropriate phosphoryl chloride. Thus, reaction with POCl will give a triester with 3 moles of the hydroxymethyl bicyclic phosphate, which is represented in the formula above when y is 3. Reaction with compounds such as ROP(O)C1 and (RO) P(O)Cl will give mixed triesters represented by the above formula where y is, respectively, 2 and l, with R representing the desired aryl radical. Preferred are those novel mixed triesters wherein x is 2 or 1 and R represents phenyl, naphthyl and mono-, dior tribromophenyl or naphthyl radicals. Preferred embodiments are specifically exemplified by radicals such as 4-bromophenyl, 2,4-dibromophenyl, l-bromo-2-naphthyl, 1,6-dibromo- 2-naphthyl and l,3,6-tribromo-2-naphthyl.

The phosphate triester flame-retardant additive of the present invention has a number of desirable properties, which render it particularly suitable for preparation of flame-retardant polyester fibers. It is soluble in molten polyester and does not adversely affect the physical properties of the finished polyester fiber. It is thermally stable at temperatures up to about 325C and has a low volatility at 250-300C, the temperatures normally employed during the melt spinning of polyester fibers. Moreover, the additive of the present invention is substantially inert in the presence of molten polyester for extended periods of time, thus minimizing polymer degradation and crosslinking.

These properties enable the flame-retardant additive of the present invention to be incorporated into molten polyester prior to extrusion of the fiber. As is known in the art, polyester fibers are conventionally prepared by the melt spinning technique whereby molten polyester is extruded under pressure through a spinneret plate having a plurality of small circular openings about 0.009 inch in diameter. The spinning is carried out at a temperature of from about 260 to 300C for poly- (ethylene terephthalate) fibers. The polymeric polyester has been previously prepared either by the batch method or by the continuous polymerization technique.

Thus, a flame-retardant additive which is thermally stable, unreactive with and soluble in molten polyester and non-volatile at spinning temperatures is particularly advantageous in that no additional fiber processing steps are required to be added to the manufacturing sequence. The additive is simply blended with the polyester melt and fibers are prepared in the usual way.

Flame-retardant polyester fibers containing the aforesaid phosphate triester exhibit a high degree of flame retardancy. However, when polyesters are blended with other fibers, particularly cellulosic fibers such as rayon, the blended fiber usually exhibits an overall reduction in flame-retardant quality. Accordingly, a further embodiment of the present invention resides in' flame-retardant polyester fibers comprising about 95 to parts of a fiber-forming linear polyester and 5 to 20 parts by weight of a two-component flameretardant additive consisting essentially of, by weight:

a. from about 20 to 80% of the aforesaid phosphate triester flame-retardant additive, and

b. from about 80 to 20% of a polychlorinated or polybrominated diaryl compound containing at least 40% by weight chlorine or bromine and having the general formula:

wherein X represents chlorine or bromine and a and a are integers the sum of which is from 3 to 10; b and 12' represent zero or 1; R represents a member selected from the group consisting of C -C alkyl radicals, C -C acyl radicals such as acetyl, phenyl and benzoyl radicals and chlorinated and brominated phenyl and benzoyl radicals; Z represents a direct bond or a member selected from the group consisting of oxygen, carbonyldioxy, sulfonyl, C -C alkylene, phenylene and chlorinated or brominated phenylene, dioxy radicals of the formula -OR O where R is C C alkylene, phenylene or chlorinated of brominated phenylene and ether linkages of the formula Cll O, Cl-l- OCHgand C6H4CH2OCH2C6H4 Examples of suitable polychlorinated and/or polybrominated compounds may be shown by the following formulas 1, II and Ill:

where X represents chlorine or bromine, a and a are integers, the sum of which is from 3 to 10, preferably 5 to 10. Preferred compounds of this group include octabromobiphenyl, hexabromobiphenyl, decabromobiphenyl and the like;

(II) Xa Xa' where X, a and a are as previously described; Z may be oxygen, carbonyldioxy, sulfonyl, C -C alkylene, phenylene, chlorinated or brominated phenylene, dioxy radicals of the formula -OR O where R is C -C alkylene, phenylene or chlorinated or brominated phenylene, or ether linkages of the formula CH O-, CH OCH and C H CH OCH C H.,. Particularly preferred compounds of this class include those wherein Z is oxygen as exemplified by the polybrominated diphenyl ethers such as decabromodiphenyl ether and hexabromodiphenyl ether or where Z is an ether linkage as described above; and

Xa Xa' where X, a, a and Z are as described previously in formula ll and R represents C -C alkyl, C C acyl radicals, phenyl and benzoyl radicals and chlorinated and brominated phenyl and benzoyl radicals. Preferred compounds of this class include tetrabromobisphenol A diacetate.

The polyesters which are rendered flame retardant in accordance with the present invention, include the fiber-forming linear saturated polyesters derived from saturated aliphatic and aromatic dicarboxylic acids and saturated diols.

These fiber-forming saturated polyesters are prepared from dicarboxylic acids such as terephthalic acid, isophthalic acid, adipic acid, bibenzoic acid,

4,4'-dicarboxyphenylmethane, 2,6- naphthalenedicarboxylic acid, 1 ,3- cyclopentanedicarboxylic acid, 1 ,3- or 1 ,4-

cyclohexanedicarboxylic acid and the like. Diols gener ally employed to prepare the fiber-forming polyesters are the saturated aliphatic, saturated cycloaliphatic or aromatic diols, preferably the lower alkane diols such as ethylene glycol, propylene glycol, and butylene glycol. Other exemplary diols include ethylene diglycol, dimethylolcyclohexane, 1,6-hexanediol, p-xylylenediol and the like. Particularly preferred are fiber-forming polyesters such as poly (ethyleneterephthalate), poly (ethylene 2,6-naphthalenedicarboxylate) or poly (1,4- cyclohexylenedimethylene terephthalate) and blends of such polyesters. These fiber-forming polyesters generally have an average molecular weight of at least about 10,000.

Generally speaking, the total amount of twocomponent flame-retardant additive which is added to the polyester is from about 5 to 20 percent based on the combined weight of polyester and additive, that is, 5 to 20 parts by weight of additive and 95 to parts by weight of polyester. These amounts provide the phosphorus, chlorine and bromine levels discussed below. The addition of amounts in excess of about 20 percent may interfere with the physical properties of the finished fiber as well as with the proper operation of the processing equipment, particularly the spinnerets used in extruding the fiber from the molten mixture of polyester and additive.

The relative amounts of phosphorus and chlorine or bromine present will, of course, be dependent on the degree of flame retardancy desired. In order to produce blends of polyester and cellulosic fibers which meet all existing standards for flame retardancy there should be present about 1 to 2 percent by weight of phosphorus in the fiber. At this phosphorus level, chlorine, if present, should be used in an amount such that the chlorine to phosphorus weight ratio is from 2:1 to 20:1. For the same level of phosphorus, that is, about 1 to 2 percent, the amount of bromine will be such that the weight ratio of bromine to phosphorus is between 2.5: and 10:1. Of course, chlorine and bromine both may be present and in such a case the chlorine to phosphorus weight ratio will be at the lower end of the aforesaid range, that is, about 2:1 to 10:1 and the bromine to phosphorus weight ratio will be about 2.5:1 to 5:1. In any event, the polyester fiber should not contain more than about 12 percent by weight of bromine as a maximum.

Polyester fibers of the present invention, which contain the aforesaid two-component flame-retardant additive, are particularly suitable for use in the preparation of blends of polyester with other fibers such as cotton, rayon, nylon, acetate, acrylics and the like. Particularly suitable are blends with cellulosic fibers such as rayon and acetate. Effectively rendering such blends flame retardant is a particular problem in the art, since under current standards the flame retardant qualities must be retained after repeated dry cleaning or laundering.

A particularly preferred embodiment resides in blends of to 90 parts by weight, preferably 40 to 60 parts by weight, of a flame-retardant polyester fiber prepared in accordance with the present invention containing the aforesaid two-component flame-retardant additive with 90 to 10 parts by weight, preferably 60 to 40 parts by weight of flame-retardant regenerated cellulose filaments or fibers, as described in US. Pat. No. 3,455,713 issued July 15, l969, to Godfrey. In brief, they are regenerated cellulose filaments having dispersed therein from 1 to 25 percent by Weight of a substantially water-insoluble cyclical and/or, linear liquid phosphonitrilic polymer having the general formula:

where R and R are the same or different alkyl or alkenyl radicals having from 1 to 6 carbon atoms and n is an integer of at least 3 and not more than about 20. These fibers are prepared by incorporating a flame retardant amount of the phosphonitrilic polymer into filament-forming viscose, and spinning and regenerating the filament.

The invention is further illustrated by the following examples, which are not to be considered as limitative of its scope. All parts and percentages are by weight based on the total weight of the composition and temperatures are in degrees centrigrade unless otherwise stated.

EXAMPLE 1 (csasonmmocaz O\P=O A slurry of 22.5 g (0.15 mole) ofa hydroxymethyl bicyclic phosphate, 4-hydroxymethyll -oxo-2,6,7-trioxal-phosphabicyclo[2.2.2]octane, 10.0 g pyridine and 300 ml THF (tetrahydrofuran) was stirred and cooled to in a nitrogen atmosphere. A solution of 34.6 g (0.125 mole) of 97% diphenyl chlorophosphate in THF was added slowly over 45 minutes. No exotherm was noticeable. After stirring and allowing the reaction mixture to warm to room temperature over a 1 hour period, the mixture was gradually heated overnight at 60C. Part of the solvent (200 ml) was removed by distillation. The reaction mixture was cooled to 10 and stirred as a precipitate formed. After about 10 minutes, 330 ml of ice water was added with stirring. The solids were collected by filtration and washed well two times with 300 ml of cold water. No chloride remained in the solid product. After drying 29.6 g (57% yield) of a white solid was obtained, mp l62-3.

The crystalline product was purified by recrystallization from reagent alcohol. White crystals were obtained, 27.4 g, mp l62-4.

- 6 Elemental Analysis: Calcd for C H O P C, 49.53, H, 4.40; P, 15.02. Found: C, 49.17; H, 4.45; P, 15.09.

EXAMPLE 2 A slurry of 55.8 g (0.31 mole) of the hydroxymethyl bicyclic phosphate used in Example I, 26.1 g of pyridine and 750 ml of THF was cooled under nitrogen to 15. A solution of 32.7 g of phenyl dichlorophosphate in 150 ml of THF was added with good stirring over a period of 1 hour. No exotherm was apparent. The mixture was stirred and heated for 4 hours during which time it became homogeneous and then a precipitate began to form. After heating overnight at 50, the solids were separated by filtration and washed four times with 400 ml of water. No chloride remained. A white powder was obtained after vacuum drying, 50.8 g (33% yield), mp 3025.

The crude product was purified by soxhlet extraction using 1 liter of acetonitrile. After 5 hours, had been extracted. After filtration, the liquid volume was reduced to 750 ml and allowed to cool in a refrigerator. The crystals that had formed were collected on a Buchner funnel and dried in vacuo, 43.5 g, mp 307-9.

Elemental Analyses: Cald. for C H O P C, 38.57; H, 4.25; P, 18.65. Found: C, 38.50; H, 4.46; P, 18.40.

EXAMPLE 3 A slurry of 16.3 g (0.092 mole) of the hydroxymethylbicyclic phosphate used in Example 1, 7.75 g pyridine and 250 ml THF was stirred and heated to 35 under nitrogen. A solution of 4.8 g (0.031 mole) of phosphorus oxychloride in 25 ml of THF was added in 5 minutes. After heating at 35 for one-half hour the mixture was heated to 50 at which point the mixture became homogeneous and a viscous lower layer began to form. After heating overnight the thick lower layer was isolated by decanting the upper phase. The lower layer was mixed well with ml of water. The solids were collected on a Buchner funnel and washed with several portions of water to remove chloride. After drying, 6.2 g (34 percent yield) of a white powder was obtained which did not melt or show signs of decomposition below 335.

P(O) 00H.

A mixture of 9.9 g (0.055 mole) of the hydroxymethyl bicyclic phosphate used in Example 1, 6.3 g (0.062 mole) triethylamine and 140 ml methylene chloride was stirred and cooled to 10C. A solution of 25.6 g of bis(4-bromophenyl) chlorophosphate, mp 5055, prepared by the method of E. N. Walsh, J. Am. Chem. Soc. 81, 3023 (1959)), in 40 ml methylene chloride was added over a 30-minute period, maintaining the temperature below 15. After the addition the mixture was allowed to warm to room temperature, refluxed for 6 hours, and stirred overnight at room temperature. The reaction mixture was filtered and the filtrate washed with water, sodium bicarbonate and sodium carbonate solution. After drying with magnesium sulfate, the methylene chloride solution was concentrated to one-half its original volume and diluted at reflux with a threefold volume of carbon tetrachloride. On cooling the product crystallized and was isolated. A portion was decolorized with charcoal and recrystallized from reagent alcohol, mp. l49-15l.

Elemental Analyses: Cald. for C H, Br O P C, 35,81;% H, 2.83; P, 10.87. Found: C, 35.58; H, 2.94; P, 10.75.

EXAMPLE To a mixture of 18.0 g (0.1 mole) of the hydroxymethyl bicyclic phosphate used in Example 1, 10.5 g triethylamine and 450 ml of methylene chloride was added with stirring a solution of 15.4 g phosphorus oxychloride in 50 ml of methylene chloride. The reaction temperature rose to 33 during the 25 minute addition period. The mixture was heated at reflux for 6 hours and then allowed to stand at room temperature overnight.

A solution of 60.4 g 1,6-dibromo-2-naphthol, 21.0 g triethylamine, and 75 ml methylene chloride was added in 15 minutes at 15. The mixture was slowly warmed to room temperature, heated at reflux for 6 hours and allowed to stand overnight at room temperature. 150 ml. of methylene chloride were removed by distillation. After cooling the solids were collected by filtration, dried and washed four times with water until no chloride was present in the washing. The solids were washed once with acetone and dried, 24.8 g, mp 3103l3.

EXAMPLE 6 The Limiting Oxygen Index (L01) of poly(ethylene terephthalate) plaques containing the phosphorus compounds of Examples l-4 was determined to demonstrate the high degree of flame retardancy they imparted.

The plaques were prepared by grinding in a mortar mixtures of poly(ethylene terephthalate) and the flame retardant additive. On top of a 6 X 6 inches stainless steel plate (l/32 inch thick) was placed a 6 X 6 inches Teflon coated aluminum plate and then a 6 X 6 inches brass frame 1/32 inch thick with a 5% X 5% inches opening. Nine grams of the powdered mixture was spread evenly on the Teflon coated aluminum plate. A woven glass fabric (4% X 5% inch) weighing 3.9-4.1 grams was placed over the mixture inside the frame. An additional 9 grams of the mixture was spread evenly over the cloth and covered with an identical Teflon coated aluminum plate and a stainless steel plate. The mold assembly was placed in a hydraulic press previously heated to 275C and the plates were closed gently at a slight pressure for 3 minutes to allow melting. The pressure was increased to 5 tons for 1 minute and then released. It was removed from the press, cooled between two large iron plates, and'carefully taken apart to remove the glass fiber support plaque, which was cut into 3 /2 X 1% inches strips.

The LOI test is made by supporting the sample strip in a U-shaped frame which is mounted in a cylindrical open chamber. Controlled mixtures of oxygen and nitrogen gases are admitted into the base of the chamber and allowed to displace the normal atmosphere. When an equilibrium atmosphere in the chamber is obtained, the sample is ignited with a butane gas flame by contacting the flame with the top edge of the sample. If the sample fails to ignite, the oxygen ratio of the atmosphere is increased to a level where the flame will just propagate. Conversely, if the sample strip ignites and the flame propagates the oxygen ratio of the atmosphere is reduced to a level where flame propagation is virtually zero. The L0] is the minimum percentage concentration of the oxygen atmosphere in which the test sample will ignite and permit flame propagation. The L0] test was introduced in 1966 (Fennimore et al., Modern Plastics, 43, 141 (1966)) and is the basis for ASTM D-2863-70. The apparatus used was the Oxygen Index Flammability Tester Model JD14 manufactured by MKM Machine Tool Company, Inc. The results are given in the table below.

Flame- Retardant Additive P LOl None 0 21.5 Ex. 1 2 27.5 Ex. 2 2 28.0 Ex. 3 2 28.8 Ex. 4 2 29.2

EXAMPLE 7 Sample No. P Halogen LOl 1 2% (Ext 1) 9.2% Cl" 30.8 2 2% (Ex. 1) 5% Br 30.8 3 2% (Ex. 1) 5% Br 30.4 4 1% (Ex. 1) 10% Br" 32.4 5 2% (Ex. 2) 5% Br 29.6

" decachlorobiphenyl was source of chlorine octa romobiphenyl was source of bromine dccabromndiphcnyl ether was source of bromine An [.01 of about 30 is desirable for polyesters which are to be blended with cellulosic fibers.

EXAMPLE 8- A mixture of 20.1 g of the compound of Example 1 and 130.9 g of poly(ethylene terephthalate) having an intrinsic viscosity of 0.62 was spun from a laboratory apparatus at 280C. Seventy-six grams of good white fiber was obtained. The intrinsic viscosity was 0.56 and tenacity was 3.75 g/den. Analysis of the fiber showed a phosphorus content of 1.98 percent by weight.

After Char Flame Length Sample (sec) (in) The vertical flame test is made by supporting a 3 X 10 inches fabric sample in a U-shaped frame which exposes 2 X 10 inches fabric. The sample and frame is.

supported vertically in a draft-free chamber with the open end of the fabric frame pointed down. Ignition of the fabric is made with a Tirrell Burner fueled with butane. A l inch long frame is aligned to the bases of the fabric so that inch of the flame bites into the fabric. Flame contact time is 12 seconds. Data are obtained to show the length of the char and the time of after flame. A sample passes the test if the average char length is 7 inches or less and no individual sample-has a char length greater than 10 inches.

What is claimed is:

l. A flame-retardant polyester fiber composition comprising from about 95 to 80 parts by weight of a fiber-forming linear polyester and, as the flameretardant additive, from about 5 to parts by weight of a phosphate triester having the formula where R is an aryl radical selected from the group consisting of phenyl and naphthyl radicals and phenyl and naphthyl radicals containing 1 to 3 chlorine or bromine atoms and substituted derivatives of said radicals, the substituents being selected from the group consisting of methyl, methoxy, phenyl, phenoxy and phenyl and phenoxy containing 1 to 5 chlorine or bromine atoms and y is an integer from 1 to 3 and x is 3-y.

2. The composition of claim 1 wherein R is selected from the group consisting of phenyl, naphthyl and phenyl and naphthyl containing 1 to 3 bromine atoms.

3. The composition of claim 1 where y is l or 2.

4. The composition of claim 1 where there is present from about 10 to 15 parts by weight of said flameretardant additive.

5. The composition of claim 1 where the polyester is a member of the group consisting of poly(ethylene terephthalate), poly( l ,4-cyclohexylenedimethylene terephthalate) and poly(ethylene 2,6-naphthalene dicarboxylate).

6. A flame-retardant polyester fiber composition comprising from about 95 to parts by weight of a fiber-forming linear polyester and 5 to 20 parts by weight of a two-component flame-retardant additive consisting essentially of, by weight:

a. from about 20 to 80 percent of a phosphate triester having the formula where R is an aryl radical selected from the group consisting of phenyl and naphthyl radicals and phenyl and napthyl radicals containing l to 3 chlorine or bromine atoms and substituted derivatives of said radicals, the substituents being selected from the group consisting of methyl, methoxy, phenyl, phenoxy and phenyl and phenoxy containing 1 to 5 chlorine or bromine atoms and y is an integer from 1 to 3 and x is 3y; and

b. from about 80 to 20 percent of a polychlorinated or polybrominated diaryl compound containing at least 40 percent by weight chlorine or bromine and having the general formula where X represents chlorine or bromine and a and a are integers the sum of which is from 3 to 10; b and b represent zero and 1; R represents a member selected from the group consisting of C -C alkyl radicals, C -C acyl radicals, phenyl and benzoyl radicals and chlorinated and brominated phenyl and benzoyl radicals; Z represents a direct bond or a member selected from the group consisting of oxygen, carbonyldioxy, sulfonyl, C -C alkylene, phenylene, and chlorinated or brominated phenylene, dioxy radicals of the formula OR O- where R is C -C alkylene, phenylene or chlorinated or brominated phenylene, or an ether link- 1 1 age of the formula CH O, CH OCH and C l-l.,CH OCH C l-l.,.

7. The composition of claim 6 wherein X represents bromine.

8. The composition of claim 7 wherein Z represents a direct bond and b and b are zero.

9. The composition of claim 8 wherein the sum of a and a is 8 to l0.

10. The composition of claim 7 where Z represents a member of the group of oxygen and ether linkages of the formula Cl-l O, CH OCH and C6H4CH2OCH2C6H4.

11. The composition of claim 6 wherein the polyester is a member of the group consisting of poly (ethylene terephthalate), poly (l,4-cyclohexylenedimethylene terephthalate) and poly (ethylene 2 ,6- naphthalenedicarboxylate).

l2. Flame-retardant yarns and fabrics comprising a combination of the flame-retardant polyester fiber of claim 1 and a member of the group consisting of cotton, rayon, nylon, acetate and acrylic fibers.

where R and R are the same or different alkyl or alkenyl radicals having 1 to 6 carbon atoms and n is an integer of at least 3.

UNITED STATES PATENT OFFICE CERTIFICATE OF CORRECTION PATENT NO. 3,883,478

DATED May 13, 1975 INVENTOR(S) John T. Gresham It is certified that error appears in the above-identified patent and that said LettersPatent are hereby corrected as shown below: In the abstract, the 5th line, flameretardant" should read --flame retardant--. Col. 1, line 33, "Moreoever' should read Moreover. Col. 3, lines 3 through 9, the general formula should read as follows:

Col. 3, lines 26 through 32, the general formula should read as follows:

Xa Xa' Col. 5, lines 16 through 23, the general formula should read as follows: t

Signed and Scaled this thirteenth Day of January 1976 A nest:

:UTH C. MANSON C. MARSHALL DANN nesting Officer Commissioner of Patents and Trademarks 

1. A FLAME-RETARDANT POLYESTER FIBER COMPOSITION COMPRISING FROM ABOUT 95 TO 80 PARTS BY WEIGHT OF A FIBER-FORMING LINER POLYESTER AND, AS THE FLAME-RETARDANT ADDITIVE, FROM ABOUT 5 TO 20 PARTS BY WEIGHT OF A PHOSPHATE TRIESTER HAVING THE FORMULA
 2. The composition of claim 1 wherein R is selected from the group consisting of phenyl, naphthyl and phenyl and naphthyl containing 1 to 3 bromine atoms.
 3. The composition of claim 1 where y is 1 or
 2. 4. The composition of claim 1 where there is present from about 10 to 15 parts by weight of said flame-retardant additive.
 5. The composition of claim 1 where the polyester is a member of the group consisting of poly(ethylene terephthalate), poly(1,4-cyclohexylenedimethylene terephthalate) and poly(ethylene 2,6-naphthalene dicarboxylate).
 6. A flame-retardant polyester fiber composition comprising from about 95 to 80 parts by weight of a fiber-forming linear polyester and 5 to 20 parts by weight of a two-component flame-retardant additive consisting essentially of, by weight: a. from about 20 to 80 percent of a phosphate triester having the formula
 7. The composition of claim 6 wherein X represents bromine.
 8. The composition of claim 7 wherein Z represents a direct bond and b and b'' are zero.
 9. The composition of claim 8 wherein the sum of a and a'' is 8 to
 10. 10. The composition of claim 7 where Z represents a member of the group of oxygen and ether linkages of the formula -CH2O-, -CH2OCH2- and C6H4CH2OCH2C6H4-.
 11. The composition of claim 6 wherein the polyester is a member of the group consisting of poly (ethylene terephthalate), poly (1,4-cyclohexylenedimethylene terephthalate) and poly (ethylene 2,6-naphtHalenedicarboxylate).
 12. Flame-retardant yarns and fabrics comprising a combination of the flame-retardant polyester fiber of claim 1 and a member of the group consisting of cotton, rayon, nylon, acetate and acrylic fibers.
 13. Flame-retardant yarns and fabrics comprising a combination of the flame-retardant polyester fiber of claim 6 and a member of the group consisting of cotton, rayon, nylon, acetate and acrylic fibers.